Product Manual
S996 is a one-component moisture curing sealant based on silicone polymer. It is a acetic clear sealant that can be used to bond glass, ceramics, stainless steel, aluminum alloy and other materials. And it is the most widely used general sealant with good elasticity and strong adhesion. It has features of low modulus, good elongation and good resilience. The surface dry time and curing speed is related to the temperature and humidity of the environment. Under high-temperature or high-humidity conditions, it will be quickly crusted. The final curing time is also related to the thickness of the glue applied.
Advantages:
S996 is a one-component moisture curing sealant based on silicone polymer. It is a acetic clear sealant that can be used to bond glass, ceramics, stainless steel, aluminum alloy and other materials. And it is the most widely used general sealant with good elasticity and strong adhesion. It has features of low modulus, good elongation and good resilience. The surface dry time and curing speed is related to the temperature and humidity of the environment. Under high-temperature or high-humidity conditions, it will be quickly crusted. The final curing time is also related to the thickness of the glue applied.
Advantages:
- Anti-UV, resisting to rain and snow weather, resisting to sun exposure, maintaining elasticity in extremely cold climates.
- Colloids are soft, elastic and have good adhesion to most materials.
- Sealing cabinets, doors and windows in interior decoration.
- Adhesive sealing of outdoor advertising boxes, windows and lighting.
- Sealing seams of sunshine top.
TDS for S996 | ||
Item | Index | Test standard |
Un-curing (test at 23ºC, 50%RH) | ||
Extrusion rate | About 300ml/min | GB/T13477.3 |
Skin time | 15min | GB/T13477.5, finger method |
Curing speed | About 2mm | 23ºCx50%RH, initial 24h |
Density | About 0.8g/cc | Test at 23ºC |
After curing (curing at 23ºC, 50%RH for 28days) | ||
Tensile modulus in 100% | About 0.45MPa | ISO37 |
Tensile strength | >1.0MPa | ISO37 |
Elongation at break | About 350% | ISO37 |
Elastic recovery rate | >96% | GB/T13477.17 |
Shore hardness | 28~32A | GB/T531.1 |
Service temperature range | -45~150ºC | -- |